Customization: | Available |
---|---|
Shape: | Fiberglass Mat |
Fiber Characteristics: | E-Glass |
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Code | Weight (g/m2) | Binder type | % L.O.I |
% Moisture content |
T. Strength (N) | |
Vertical | Horizontal | |||||
EMC100 | 100 | Powder/Emulsion | 4.0-12.0 | ≤0.2 | ≥80 | ≥80 |
EMC120 | 120 | Powder/Emulsion | 4.0-12.0 | ≤0.2 | ≥80 | ≥80 |
EMC150 | 150 | Powder/Emulsion | 4.0-12.0 | ≤0.2 | ≥100 | ≥100 |
EMC200 | 200 | Powder/Emulsion | 4.0-12.0 | ≤0.2 | ≥100 | ≥100 |
EMC225 | 225 | Powder/Emulsion | 2.0-8.0 | ≤0.2 | ≥100 | ≥100 |
EMC300 | 300 | Powder/Emulsion | 2.0-8.0 | ≤0.2 | ≥120 | ≥120 |
EMC380 | 380 | Powder/Emulsion | 2.0-8.0 | ≤0.2 | ≥120 | ≥120 |
EMC450 | 450 | Powder/Emulsion | 2.0-8.0 | ≤0.2 | ≥150 | ≥150 |
EMC600 | 600 | Powder/Emulsion | 2.0-8.0 | ≤0.2 | ≥150 | ≥150 |
1.Uniform density ensures consistent fiberglass content and mechanical properties of the composites products;
2.Excellent flexibility ensures good moldability with no spring-back at sharp corners;
3.Fast and consistent wet-out speed in resins and rapid air release reduce resin consumption, improving manufacturing costs;
4.The composite products have high dry and wet tensile strength and good transparency.
Application
Fiberglass chopped strands mat are mainly used in the fields of FRP products with three major process such as hand lay-up, filament winding and molding process. E-glass fiberglass chopped strand mat, owing to its excellent performance, is widely used in various applications, such as ship building, aviation manufacturing, auto manufacturing, home furnishing, etc.
Packing
Fiberglass chopped strand mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
Storage
The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15ºC to 35ºC and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.
Best used within 12 months after production date. Fiberglass products should remain in their original packaging until just prior to use.