Best Selling Hfcp Fiberglass Reinforced Composite Sheet for Automotive Trim

• Customization: Available
• Fiberglass Type: E-Glass
• Certification: BSCI, CCC, CE, FCC, GS, ISO, RoHS, SAA
• Transport Package: Inner PE Bag, Outer Cartons with Pallet
• Specification: 1200g
• Trademark: NJEFG
• Origin: China
• HS Code: 8546900000
• Production Capacity: 100000000sqm/Year
• Package Size: 50.00cm * 60.00cm * 40.00cm
• Package Gross Weight: 10.000kg

Product Description

PRODUCT DESCRIPTION

The HFCP Reinforced Composite Sheet use PP fiber and glass fiber as the main raw materials, firstly been produced into composite mat by wet lay-out process or dry process. Then in next process, pressure the composite mat with high pressure and high temperature, the mat become sheets. This composite sheet has the advantages of low density, flame retardancy , high/low - temperature resistance, flexible and beautiful design, waterproofing, easy coating, high strength and low cost. Comparing to steel sheets or FRP boards, this composite board is characterized by light weight, impact resistance,  vibration resistance, thermal insulation, size stability, easy forming, acoustic absorption, no smell, anti mildew, good toughness, corrosion resistance, flexible and low price. The surface of the sheet can be selected according to the actual requirements of different surface coverings, such as: rubber film, barrier film, decoration, hard polypropylene film, non-woven cloth, reinforced material or no coverings.

The HFCP Reinforced Composite Sheet is idea material in the field of automobile manufacture, many parts of the cars can be produced by this composite sheet including car roof, top and bottom decoration board of a,b,c column, cover plate, coat rack, outer wheel covers of four wheels , trunk cover, bottom plate of engine, back boards of seat and so on.

CHARACTERISTICS  

1. light weight   Flame retardant 
2. Table size   High/low - temperature resistance
3. Acoustic absorption  Anti mildew

TECHNICAL DATA                
HFCP materials specifications ( regular )
Area weight from 700-2000g/m2
Width:≤2500mm
Length: as per request
 

Weight             (g/m2)	Tensile strength             (Mpa)	Winding        (Mpa)	Density
700	7.8	860	0.338
800	9	1215	0.378
900	9.5	1450	0.418
1000	15	1800	0.458
1200	18.5	2000	0.504
1400	27.5	2600	0.603
1600	40	3400	0.711
2000	47	4800	0.848

HFCP mechanical property (2.5 mm thick length of sheet molded at 23 degrees Celsius)
 

HFCP sheet	Thickness          (before compressing)	Thickness         (after compressing)	Thickness range          of mould pressing
(g/m2)	(mm)	(mm)	(mm)
600	1.8-2.1	4.0-4.5	1.5-3.5
700	2.5-2.8	4.5-5.0	1.5-3.5
800	2.5-3.0	4.7-5.2	1.5-4.0
900	3.0-3.5	5.3-5.8	2.0-4.5
1000	3.2-4.0	6.0-6.5	2.0-5.0
1200	4.0-4.9	7.2-7.7	2.0-6.0
1400	5.0-6.2	8.5-9.0	2.0-7.0
1600	5.5-6.5	9.5-10.0	2.0-8.0
1800	6.0-7.0	10.5-11.0	2.0-9.0
2000	6.5-7.5	11.0-12.5	2.0-11.0

Remark: 1. The technical data above is for reference only
2. Any special size can also be supplied according to customers' request
­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­
PACKING
Inner PE bag, Outer Cartons with Pallet
­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­­
STORAGE
This product should be stored in a dry, ventilated and rainproof place,(with temperatures from 5ºCto 35ºC and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.